Author
Aljashaami, Dhyai Hassan Jawad, Ghobadlou, Ali Hosseinzadeh, Yapıcı, Güney Güven
Publication Date
2019-09
Publication Place
-
IOP Publishing
Subject
Layered composite, Accumulative roll bonding, Aluminum, Severe plastic deformation, Cyclic strength, Fatigue properties
Type
Periodical
Language
English
Digital
Yes
Manuscript
No
Library
Özyeğin University
Library Asset ID
2053-1591
Record ID
d1cca7db-7ac9-462c-bbcc-053d47740dca
Library Location
Mechanical Engineering
Date
2019-09
Notes
Ozyegin University
Sample Text
Multi-layered composites have received great interest due to their enhanced mechanical and physical properties. In this study, Al6061/Al2024 composites were processed by accumulative roll bonding as a severe plastic deformation technique. The processed structure after four cycles contained alternating layers of both aluminum compositions. For outlining the mechanical behavior, uniaxial deformation experiments in the monotonic and cyclic regime were performed. With increased number of processing cycles, decent progress in hardness levels was exhibited with varying degrees among constituent alloys. Accordingly, improvement levels of up to 1.5 and 2 times were recorded for Al2024 and Al6061 layers, respectively. The tensile strength of the bi-metallic composite reached over 320 MPa after two cycles, coinciding with more than two-fold of the weaker base composition. Fatigue strength was also improved, especially at the low cycle regime. Microstructural observations revealed the level of refinement down to sub-micron scale along with possible fracture mechanisms under tensile straining.
DOI
10.1088/2053-1591/ab2d93
Cilt
6